CERALENE®
grade		 wax type appearance density (at 23°C)
g/cm3		 drop point
°C		 viscosity ¹
(at 120°C) mPa · s		 penetration
(at 25°C) mm · 10-1		 acid value
mg KOH/g
non-oxidized
1X LDPE white prills 0.92 - 0.94 102 160 2 - 3 < 0.5
1M LDPE white prills 0.92 - 0.94 104 260 4 - 6 < 0.3
2E LDPE white prills 0.92 - 0.94 106 550 ≤ 2 0
2T LDPE white prills 0.92 - 0.94 108 1.100 1 - 3 0
882 Polyolefine white prills 0.90 - 0.93 146 280** ≤ 0.5 0
1H HDPE white prills 0.94 - 0.96 122 1.000* ≤ 2 0
oxidized
326 Oxid. PE white powder 0.94 - 0.96 137 ² 110.000** ≤ 0.5 28
719 Oxid. PE white powder 0.94 - 0.96 138 ² 140.000** ≤ 0.5 19
functionalised
592 Polyester mod. white prills 0.96 - 0.98 60 550 n.d. 11
620 Grafted PE yellowish prills 0.96 - 0.99 108 60 ≤ 1 20
630 Grafted PE yellowish prills 0.96 - 0.97 109 70 ≤ 1 30
677 Polyester mod. almost white prills 0.96 - 0.99 72 700 6 35
691 Polyester mod. white prills 0.96 - 0.98 73 130 1 - 2 10
692 C Polyester mod./ white prills 0.96 - 0.98 59 500 n.d. 12
cosmic grade
693 Polyester mod. white prills 0.96 - 0.98 71 400 1 - 2 16
694 Polyester mod. white prills 0.96 - 0.98 70 170 1 - 2 19
695 Polyester mod. yellowish prills 0.96 - 0.99 79 170 n.d. 9
696 Polyester mod. yellowish prills 0.96 - 0.99 88 150 n.d. 7
697 Polyester mod. yellowish prills 0.96 - 0.99 91 160 n.d. 5
 

1) Haake Rheostress Viscosimeter
2) melting temperature (DSC)
* at T=140 °C
** at T=150 °C
n.d.: not determined/applicable

CERALENE® types for a broad range of industrial applications

CERALENE® masterbatch technical
resins		 PVC duroplasts
power coatings		 bitumen hotmelt
adhesive
(viscosity
adaption)		 wood/fibre-plastic
composites
(adhesion
promotion)		 solvent based
formulations
(slip abrasion
resistance)		 water-based
additives
(surface
modification)
non-oxidized
1X O O ++ ++ O ²
1M + + ++ ²
2E ++ ++ ++ ²
2T ++ + ++ ++ O ²
882 ++ + O
1H ++
oxidized
326 ++ ++
719 + ++
functionalised
592 ++ + ++ +
620 O + ++ ++
630 O + ++ ++
677 + ++ +
691 ++ ++ + + + ++
692 C in cosmetics – especially for the manufacturing of lip sticks
693 ++ ++ ++ + + + ++
694 ++ ++ ++ + + + ++
695 O ++ +
696 O ++ +
697 ++ +
 

1) Haake Rheostress Viscosimeter
2) inks
O suitable
+ recommended
++ specially recommended

CERALENE® waxes for plunger lubrication

Use as high performance plunger lubricant for aluminium die-casting machines.

CERALENE® wax type appearance particle size
(mm)		 drop point
°C		 viscosity ¹
(at 120°C) mPa · s		 penetration
(25°C) mm · 10-1
2E 450/2000 LDPE white 0.45-2.0 106 360 ≤ 2
DCG LDPE/graphite black 0.45-2.0 108 600 ≤ 2
 

New synthetic CERALENE® 691, 693, 694, 592 polyester waxes

Overview

CERALENE® drop point
°C		 acide value
mg KOH/g		 viscosity
(at 120°C) mPa · s
691 73 10 130
693 71 16 400
694 70 19 170